Iso 527 2 is an international standard for determining the tensile properties of reinforced and non reinforced plastics.
Plastic tensile test standard.
Tensile strength maximum tensile stress.
Properties that are directly measured via a tensile test are ultimate tensile strength breaking strength maximum elongation and reduction in area.
The test method can be used for testing materials up to 14mm 0 55 in and the material should be in the shape of a dumbbell or dog bone.
Test conditions for moulding and extrusion plastics technical corrigendum 1 95 99 iso tc 61 sc 2.
A universal testing machine tensile testing machine is needed to perform this test.
Learn about the international material testing standards for plastics and rubber and find out which standards apply to your products.
Astm d638 is the most common testing standard for determining the tensile properties of reinforced and non reinforced plastics.
Din en iso 527.
Standard test method for tensile impact energy to break plastics and electrical insulating materials.
From these measurements the following properties can also be determined.
Tensile testing of plastics supplies the data for a sample.
Tensile testing also known as tension testing is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure.
While it provides similar results to astm d638 iso 527 2 is not considered technically equivalent due to differences in specimen size and test requirements while some large multinational manufacturers test to both astm d638 and iso 527 2 most of our customers demonstrate a.
With the use of plastics being at an all time high it is critical that manufacturers be able to properly gauge the mechanical strength of their materials.
1 1 this test method covers the determination of the tensile properties of unreinforced and reinforced plastics in the form of standard dumbbell shaped test specimens when tested under defined conditions of pretreatment temperature humidity and testing machine speed.
Tensile tests are used for example in the validation of the chemical resistance of plastics since the results of this test disclose even extremely small changes in the material.
This test method uses standard dumbell or dogbone shaped specimens under 14mm of thickness.
Astm d638 is one of the most common plastic strength specifications and covers the tensile properties of unreinforced and reinforced plastics.
This includes astm d638 technically equivalent to iso 527 1 is a testing standard which ascertains the tensile properties of a plastic material.